Major Features 主要優(yōu)點(diǎn)
Long open time 操作時(shí)間長(zhǎng)
High shear and peel strength 高的剪切與高剝離強(qiáng)度
Excellent low temperature properties 優(yōu)異的低溫性能
Room temperature cure 常溫固化
Controlled flow 流動(dòng)性容易控制
PROPERTIES OF UNCURED MATERIAL 固化前材料性能
|
Property性能
|
Test Method測(cè)試方法
|
800A
|
800B
|
|
Color/appearance
顏色
|
Visual
目視
|
Creamy white, viscous/liquid
膏狀白色粘稠液體
|
Amber Liquid
琥珀色液體
|
|
SpecificGrav密度, g/cc
|
ASTM D-792
|
1.12
|
1.10
|
|
Viscosity粘度(cP), 25ºC
|
ASTM D-2393
|
60,000 - 100,000
|
8,000 - 12,000
|
TYPICAL CURED PROPERTIES 固化后屬性
|
Property
性能
|
Test Method
測(cè)試方法
|
Test Value
測(cè)試值
|
|
Hardness, casting after 15 minutes, Shore D 邵氏硬度，澆鑄15分鐘后
|
D-2240
|
75
|
|
Ultimate Tensile Strength
極限抗張強(qiáng)度, psi
|
D-638
|
5200
|
|
Elongation 生長(zhǎng)率, %
|
D-638
|
7
|
|
Modulus 模量(psi)
|
D-638
|
400, 000
|
|
T- Peel Test 剝離測(cè)試(pli)
|
D-1876
|
50-60
|
|
Lap shear strength 搭接剪切強(qiáng)度, psi at 25C
|
ASTM D-1002
|
|
|
Galvanized Steel 鍍鋅鋼
|
|
2500
|
|
Fibre reinforced composite 纖維增強(qiáng)復(fù)合材料
|
|
1500
|
|
Mineral filled PET plastics 礦物填充PET塑料
|
|
800
|
|
Aluminum (primered) 鋁
|
|
5000
|
|
Aluminum (acid etched) 鋁（酸腐蝕）
|
|
4200
|
Effects of application temperature on lap shear strength(LSS ) by ASTM D-1002
溫度對(duì)搭接剪切的影響
Load applied 10 minutes after specimens reach test temperature當(dāng)樣品達(dá)到測(cè)試溫度后10分鐘
|
|
Test Temperature
|
LSS Value, psi
|
|
Al/Al
|
-60ºC
|
4700
|
|
Al/Al
|
82 ºC
|
1500
|
|
Al/Al
|
121 ºC
|
500
|
|
Al/Al
|
30 days salt spray
|
4000
|
|
Al/Al
|
30 days @ 60ºC/100% RH
|
3500
|
Directions for use使用方法
|
Reaction Ratio (by weight) 反應(yīng)重量比
|
|
100A/49B
|
|
Reaction Ratio (by volume) 反應(yīng)體積比
|
|
100A/50B
|
|
Pot Life (100 grams) 25°C 使用時(shí)間（100克）
|
ASTM D-2471
|
30 minutes
|
|
Pot Life (20 grams) 25°C 使用時(shí)間（20克）
|
|
60 minutes
|
Curing time table固化進(jìn)度表:
3-5 days at 77?F. or elevated temperatures for accelerated cure. 在25攝氏度下3-5天。或者在升高的溫度下
加速固化
Shelf Life 保質(zhì)期
Provided this material is stored under the recommended storage condition in the original container, it will remain in useable condition for
from date of shipping.
若該產(chǎn)品按照上述要求存儲(chǔ)，并且是保存在原裝容器內(nèi)，從發(fā)貨之日起，在一年內(nèi)可以使用。